Retroreflective articles comprising olefinic seal films

ABSTRACT

Microstructured articles, such as a retroreflective articles, having a plurality of (e.g. cube-corner) microstructured elements and a seal film layer adhered to portions of the cube-corner elements and/or portions of a (e.g. flexible) body layer. The seal film is a thermoplastic polymeric material comprising reaction products of alkylene in an amount of at least about 50% and reaction products of at least one non-acidic polar monomer.

BACKGROUND

Retroreflective sheetings have the ability to redirect incident lighttowards its originating source. This ability has led to the wide-spreaduse of retroreflective sheetings on a variety of articles. There areessentially two types of retroreflective sheeting: beaded sheeting andcube-corner sheeting. Beaded sheeting employs a multitude of glass orceramic microspheres to retroreflect incident light. Cube-cornersheeting, on the other hand, typically employs a multitude of rigid,interconnected, cube-corner elements to retroreflect incident light.

A specular reflective coating such as a metallic coating can be placedon the backside of the cube-corner elements to promote retroreflection.In addition to or in lieu of a metallic coating, a seal film can beapplied to the backside of the cube-corner elements. The sealing filmmaintains an air interface at the backside of the cubes to enhanceretroreflectivity.

Various sealing films suitable for use with flexible retroreflectivesheeting have been described. See for example U.S. Pat. Nos. 5,784,197;5,691,846; and 6,318,867.

SUMMARY

In one embodiment, a flexible retroreflective article is describedcomprising a polymeric light transmissive body layer having an elasticmodulus of less than 7×10⁸ pascals and a plurality of cube-cornerelements projecting from a major surface of the body layer; and a sealfilm adhered to portions of the body layer.

In another embodiment, a (e.g. retroreflective) microstructured articleis described that comprises a plurality of (e.g. cube-corner)microstructured elements and a seal film layer adhered to portions ofthe cube-corner elements.

In each of these embodiments, the seal film is a thermoplastic polymericmaterial comprising reaction products of (e.g. ethylene) alkylene in anamount of at least about 50% and reaction products of at least onenon-acidic polar comonomer such as vinyl acetate, alkyl(meth)acrylatemonomers, and mixtures thereof. The thermoplastic polymeric material ofthe seal film may optionally further comprise acid modification,anhydride modification, carbon monoxide modification, and combinationsthereof. The alkylene of the thermoplastic material comprises 2 to 8carbon atoms and more typically 2 to 3 carbon atoms. The alkyl of thealkyl(meth)acrylate typically comprises 1 to 8 carbon atoms and moretypically 1 to 4 carbon atoms.

In some aspects, the seal film comprises a copolymer or terpolymer ofalkylene and at least one comonomer selected from vinyl acetate;alkyl(meth)acrylate monomers, and mixtures thereof. The copolymer orterpolymers typically comprises about 5 wt-% to about 40 wt-% of vinylacetate, alkyl(meth)acrylate monomers, and mixtures thereof. The sealfilm may be selected from an anhydride modified alkylene (meth)acrylatepolymer, an acid modified alkylene (meth)acrylate polymer, anacid/acrylate modified ethylene vinyl acetate polymer, an alkylene vinylacetate carbon monoxide copolymer, and mixtures thereof.

In other aspects, the seal film comprises a blend of at least twothermoplastic polymers and the blend comprises reaction products ofalkylene in an amount of at least about 50% and reaction products of atleast one non-acidic polar comonomer such as vinyl acetate,alkyl(meth)acrylate monomers, and mixtures thereof. The seal film may bemonolithic (i.e. a single layer) or multilayered, having a seal filmlayer disposed between the cube-corner elements and one or moreadditional film layers.

In another embodiment, a method of making a retroreflective article isdescribed comprising thermally bonding the seal film to at leastportions of the body layer.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1A is a cross-sectional view of an embodiment of cube-cornerretroreflective sheeting including a sealing film.

FIG. 1B is a cross-sectional view of an embodiment of cube-cornerretroreflective sheeting including a multilayered sealing film.

FIG. 2 is a perspective view of an embodiment of cube-cornerretroreflective sheeting.

FIG. 3 is a perspective view of an embodied cube-corner surface.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

The invention relates to microstructured (e.g. cube-cornerretroreflective) articles including a seal film (also referred to as asealing film) that substantially covers the microstructured surface. Insome embodiments, the microstructures are provided on a (e.g. flexible)body layer. The microstructures and the body layer are typically lighttransmissive. The seal film is typically bonded to portions of the bodylayer and/or (e.g. cube-corner microstructured surface. Although thepresent invention will be described with reference to (e.g. flexible)retroreflective sheeting, the seal film described herein may be suitablefor bonding to other microstructured surfaces as well.

The term “microstructure” is used herein as defined and explained inU.S. Pat. No. 4,576,850. Microstructures are generally discontinuitiessuch as projections and indentations in the surface of an article thatdeviate in profile from an average center line drawn through themicrostructure such that the sum of the areas embraced by the surfaceprofile above the center line is equal to the sum of the areas below theline, the line being essentially parallel to the nominal surface(bearing the microstructure) of the article. The heights of thedeviations will typically be about +/−0.005 to +/−750 microns, asmeasured by an optical or electron microscope, through a representativecharacteristic length of the surface, e.g., 1-30 cm. The average centerline can be plano, concave, convex, aspheric or combinations thereof.Articles where the deviations are of low order, e.g., from+/−0.005+/−0.1 or, preferably, +/−0.05 microns, and the deviations areof infrequent or minimal occurrence, i.e., the surface is free of anysignificant discontinuities, can be considered to have an essentially“flat” or “smooth” surface. Other articles have deviations are ofhigh-order, e.g., from +/−0.1 to +/−750 microns, and attributable tomicrostructure comprising a plurality of utilitarian discontinuitieswhich are the same or different and spaced apart or contiguous in arandom or ordered manner.

With reference to FIGS. 1A and 1B, exemplary cube-corner retroreflectivesheeting 10 comprises a multitude of cube-corner elements 12 and a bodylayer 18. Body layer 18 may also be referred to as an overlay film aswell as a base substrate. Body layer 18 typically has a thickness of atleast 20 micrometers and more typically at least 50 micrometer. Bodylayer 18 usually has a thickness less than 1,000 micrometer, andtypically no greater than 250 micrometers. The cube-corner elements 12project from a first, typically rear side of body layer 18.

The cube-corner elements and body layer are typically formed from alight transmissive polymeric material. This means that the polymer isable to transmit at least 70 percent of the intensity of the lightincident upon it at a given wavelength. More preferably, the polymersthat are used in the retroreflective sheeting of the invention have alight transmissibility of greater than 80 percent, and more preferablygreater than 90 percent. When the retroreflective sheeting is employedfor uses other than traffic safety, such as advertising displays, thelight transmissibility may be as low as 5 to 10 percent.

In a preferred embodiment, the body layer 18 is the outermost layer onthe front side of the sheeting 10. As shown in FIG. 1, light enters thecube-corner sheeting 10 through the front surface 21. The light thenpasses through the body portion 18 and strikes the planar faces of thecube-corner elements 12 and returns in the direction from which it cameas shown by arrow 23. The body layer 18 functions to protect thesheeting from outdoor environmental elements and/or provides mechanicalintegrity to the sheeting.

The cube-corner retroreflective sheeting may include a land layer suchas shown in U.S. Pat. No. 5,450,235. In some embodiments, the land layeris integral with the cube-corner elements meaning that the land andcubes are formed from a single polymeric material—not two differentpolymeric layers subsequently united together. Particularly forembodiments, wherein the retroreflective sheeting is flexible, the landlayer 16, typically, has a thickness in the range of about 0 to 150micrometers, and preferably in the range of approximately about 1 to 100micrometers. The thickness of the land is preferably no greater than 10percent of the height of the cube corner elements, and more preferablyabout 1 to 5 percent thereof. In sheetings having thicker land portions,it is typically more difficult to achieve decoupling of individual cubecorner elements.

The cube-corner elements 12 typically have a height in the range ofabout 20 to 500 micrometers, and more typically in the range of about 35to 100 micrometers. Although the embodiment of the invention shown inFIG. 1 has a single body layer 18, it is within the scope of the presentinvention to provide more than one body layer 18 (e.g. a multi-layerbody). A seal film 30 is bonded to the (e.g. cube-corner) structuredsurface, i.e. on the opposite side of the body layer film. The seal filmtypically functions to maintain an air interface with the (e.g.backside) of the cube-corner elements to enhance retroreflectivity. Sealfilms can also be employed to impart color or protect the cube-cornerelements from environmental factors.

As shown in FIG. 2, a network of narrow intersecting bonds 14 extendover the entire (e.g. back) surface. The pattern of sealing regions orlegs thereby creates cells 16. The sealing regions can form variouspatterns that often are contiguous polygons such as parallelograms,triangles, and hexagons.

The sheeting can also include a seal coat as described in U.S. Pat. No.5,784,197, a backing and/or an adhesive layer on the seal film in orderthat the cube-corner retroreflective sheeting can be secured to asubstrate.

FIG. 3 illustrates a perspective view of the cube-corner element surfacewhich is typically the back side of the article. As shown, thecube-corner elements 12 are disposed as matched pairs in an array on oneside of the sheeting. Each cube-corner element 12 has the shape of atrihedral prism with three exposed planar faces 22. The planar faces 22may be substantially perpendicular to one another (as in the corner of aroom) with the apex 24 of the prism vertically aligned with the centerof the base. The angle between the faces 22 typically is the same foreach cube-corner element in the array and will be about 90 degrees. Theangle, however, can deviate from 90 degrees as is well-known. See, forexample, U.S. Pat. No. 4,775,219 to Appledorn et al. Although the apex24 of each cube-corner element 12 may be vertically aligned with thecenter of the base of the cube-corner element, see, for example, U.S.Pat. No. 3,684,348. The apex also may be canted to the center of thebase as disclosed in U.S. Pat. No. 4,588,258. The present invention isnot limited to any particular cube-corner geometry. Various cube-cornerconfigurations are known such as described in U.S. Pat. Nos. 4,938,563,4,775,219, 4,243,618, 4,202,600, and 3,712,706. The cube-cornerconfigurations described in U.S. Pat. No. 4,588,258 can provide wideangle retroreflection among multiple viewing planes.

A specular reflective coating such as a metallic coating (not shown) canalso optionally be placed on the backside of the cube-corner elements topromote retroreflection. The metallic coating can be applied by knowntechniques such as vapor depositing or chemically depositing a metalsuch as aluminum, silver, or nickel. A primer layer may be applied tothe backside of the cube-corner elements to promote the adherence of themetallic coating.

Presently described are seal films for (e.g. flexible) retroreflectivearticles. The seal film is a thermoplastic polymeric material comprisingreaction products of alkylene in combination with reaction products ofat least one non-acidic monomer.

The alkylene component is low cost and provides durability (e.g.chemical resistance and cold temperature impact resistance) to the sealfilms. The amount of alkylene of the polymeric material of the seal filmis typically at least about 50% by weight. In some embodiment, theamount of alkylene is 55 wt-%, 60 wt-%, 65% wt-%, 70 wt-%, 75 wt-%, or80 wt-%. Alkylene components having two (i.e. ethylene) to eight (i.e.octene) carbon atoms are typically employed in the manufacture of filmswith ethylene, and (iso)propylene to a lesser extent, being the mostcommon.

The non-acidic monomer improves the adhesion of the seal film to thebody layer and/or cube-corner elements. The non-acidic monomer reactionproducts typically total at least 1 wt-% and more typically at least 10wt-%. Further, the total amount of non-acidic comonomer reactionproducts generally ranges up to about 40 wt %. The total amount ofnon-acidic comonomer reaction products may range up to about 32 wt-%, or25 wt-%, particularly when the seal film is monolithic (i.e. a singlelayer).

Preferred non-acidic monomers include vinyl acetate and alkyl(meth)acrylate. Vinyl acetate has the structure CH₃COOCH═CH₂; whereas(meth)acrylate monomers are a class of monomers having a polymerizableCH₂═CH— (i.e. acrylate) group or a terminal CH₂═C(CH₃)— (i.e.methacrylate group). Acrylate tends to be preferred since such group ismore reactive than a methacrylate group. Alkyl(meth)acrylate monomershave the general structure CH₂═CHCOOC_(n)H_(2n-1). Although, n may rangefrom 1 to 12, n is commonly no greater than 8 with methyl acrylateCH₂═CHCOOCH₃, ethyl acrylate CH₂═CHCOOC₂H₅, methyl methacrylateCH₂═C(CH₃)COOCH₃, and ethyl methacrylate CH₂═C(CH₃)COOC₂H₅ being mostcommonly employed in the manufacture of films.

In one embodiment, the seal film comprises a copolymer or terpolymer ofalkylene and at least one comonomer selected from vinyl acetate,alkyl(meth)acrylate monomers, and the various comonomer mixturesthereof. Accordingly, the seal film may comprise of reaction products ofalkylene and vinyl acetate, alkylene and a single alkyl(meth)acrylatemonomer, alkylene and a combination of vinyl acetate and at least onealkyl(meth)acrylate monomer, alkylene and a combinations of two or morealkyl(meth)acrylate monomers.

The thermoplastic polymeric material of the seal film may optionallycomprise acid modification, anhydride modification, carbon monoxidemodification, and combinations thereof. For example, the seal film maycomprise a terpolymer of alkylene; at least one comonomer selected fromvinyl acetate, alkyl(meth)acrylate monomers, and mixtures thereof, andat least one additional comonomer including for example acrylic acidH₂C═CHCOOH, methacrylic acid H₂C═C(CH₃)COOH, (meth)acrylic acid (e.g.maleic) anhydride, carbon monoxide, and mixtures thereof The amount ofsuch additional comonomer typically ranges up to about 10 wt-%

In general, as the percentage of alkylene is decreased, the percentageof non-acidic polar monomer is increased, thereby increasing the sealfilm's flexibility. However, the inclusion of small amount of acidic oranhydride modification can decrease the flexibility in comparison to acopolymer having the same amount of non-acid polar comonomer.

Suitable copolymers include copolymers of ethylene with vinyl acetate(EVA); acid- or anhydride-modified EVAs; other modified EVAs, such asacid or anhydride-/acrylate-modified EVAs; ethylene ethyl acrylatecopolymers (EEA); ethylene methyl acrylate copolymers (EMA); acid- oranhydride-modified ethylene acrylate materials (AEA); ethylene vinylacetate, carbon monoxide terpolymers (EVACO); ethylene, butyl acrylate,carbon monoxide terpolymers (EBACO); and ethylene n-butyl acrylatecopolymers (EnBA).

Suitable EVAs (copolymers of ethylene with vinyl acetate) for use inseal films of the present invention include resins from DuPont availableunder the trade designation “Elvax”. Typical grades range in vinylacetate content from 9 to 40 weight percent and in melt index from 0.3to 500 dg/min. (per ASTM D1238). Suitable EVAs also include high vinylacetate ethylene copolymers from Equistar available under the tradedesignation “Ultrathene”. Typical grades range in vinyl acetate contentfrom 12 to 18 weight percent. Suitable EVAs also include EVA copolymersfrom AT Plastics available under the trade designation ATEVA. Typicalgrades range in vinyl acetate content from 2 to 26 weight percent.

Exemplary commercially available seal film materials are depicted in thefollowing table:

Vicat Trade Melt Index Softening Point Melt Point Generic ChemicalDescription Designation Comonomer (ASTM D1238) (ASTM D1525) (ASTM D3417)ethylene-vinyl acetate copolymer “Elvax 12%, by wt, 8 g/10 min 71° C.(160° F.) 95° C. (203° F.) resin 3134Q” vinyl acetate ethylene-vinylacetate copolymer “Elvax 9%, by wt, 7 g/10 min 77° C. (171° F.) 98° C.(208° F.) resin 3124” vinyl acetate ethylene vinyl-acetate copolymer“Elvax 18%, by wt, 2.5 g/10 min 65° C. (149° F.) 87° C. (189° F.) resin3170” vinyl acetate ethylene-vinyl acetate copolymer “Elvax 18%, by wt,8 g/10 min 61° C. (142°) 86° C. (149°) resin 3174” vinyl acetateethylene-vinyl acetate copolymer “Elvax 25%, by wt, 2 g/10 min 52° C.(126 F.) 77° C. (171° F.) resin 3190” vinyl acetate anhydride-modifiedethylene “Bynel 7.3 g/10 min 122° F. 181° F. acrylate polymer 21E533”modified ethylene acrylate resins “DuPont 8 dg/min 54° C. (129° F.) 92°C. (198° F.) Bynel 22E757” acid/acrylate-modified ethylene “DuPont 3.2dg/min 65° C. (149° F.) 87° C. (189° F.) vinyl acetate polymers Bynel3101” acid/acrylate-modified ethylene “Bynel 9.5 dg/min 57° C. (135° F.)87° C. (189° F.) vinyl acetate polymers 3120” acid/acrylate-modifiedethylene “Bynel 8.1 dg/min 60° C. (140° F.) 87° C. (189° F.) vinylacetate polymers 3126” acid-modified ethylene acrylate “Bynel 10 dg/min60° C. (140° F.) 91° C. (196° F.) polymers with medium to high 2002”acid comonomer contents acid-modified ethylene acrylate “Bynel 2014 7.9dg/min 57° C. (135° F.) 86° C. (187° F.) polymers with medium to highASTM D1238 acid comonomer contents acid-modified ethylene acrylate“Bynel 2022 35 dg/min 58° C. (136° F.) 87° C. (189° F.) polymers withmedium to high acid comonomer contents

In another embodiment, the seal film comprises a blend of at least twodifferent thermoplastic polymers. The thermoplastic polymers of theblend typically differ with respect to the type of comonomer and/or theamount of comonomer and/or the molecular weight (e.g. melt flow index).The blend may comprise two or more homopolymer(s), copolymer(s), orterpolymers(s). In such embodiments, the blend comprises reactionproducts of alkylene in an amount of at least about 50% in combinationwith reaction products of vinyl acetate, alkyl(meth)acrylate monomers,and mixtures thereof.

In some aspects, each of the polymers of the blend comprise reactionproducts of alkylene in an amount at least about 50% in combination withreaction products of vinyl acetate, alkyl(meth)acrylate monomers, andmixtures thereof.

In other aspects, the blend comprises a first polymer that comprisesreaction products of alkylene in an amount at least about 50% incombination with reaction products of vinyl acetate, alkyl(meth)acrylatemonomers, and mixtures thereof, and a second polymer that does notinclude reaction products of vinyl acetate, alkyl(meth)acrylatemonomers, and mixtures thereof. The second polymer is typically apolyolefin, comprising a major amount of alkylene (as previouslydescribed). Suitable polyolefins include ionomeric ethylene copolymers(e.g. SURLYN-8920 and SURLYN-9910), low density polyethylenes, andpolyethylene copolymers including acid functional polymers such aspoly(ethylene-co-acrylic acid) “EAA”, poly(ethylene-co-methacrylic acid)“EMA”, poly(ethylene-co-maleic acid), and poly(ethylene-co-fumaricacid). Alternatively the second polymer may be a compatible polyurethanepolymer.

The seal film can be monolithic, i.e. a single (substantiallyhomogeneous) layer, as depicted in FIG. 1A. Alternatively, as depictedin FIG. 1B, the seal film can be multilayered, comprising a seal filmlayer 31 in contact with at least the body layer or cube-corner elementsand an (e.g. outer) second film layer 32. The second film layer 32 mayalso comprise reaction products of alkylene in an amount of at leastabout 50% in combination with reaction products of vinyl acetate,alkyl(meth)acrylate monomers, and mixtures thereof. However, the secondfilm layer typically differs from the seal film layer. For example, thesecond film layer may have a different melt flow index, a higheralkylene content and/or different additives such as pigment. The secondfilm layer may comprise a polyolefin, as just described with respect tothe blends. If the second film layer is dissimilar to the seal filmlayer, a tie layer 33 may be provided between the seal film layer andsecond layer.

In some embodiments, such as when a monolithic seal film is employed,the seal film has a melt point of at least about 70° C., 75° C., or 80°C. as measured according to ASTM D 3418. Having a sufficiently high meltpoint or Vicat softening point can be important to insure that the sealfilm does not deform when exposed to elevated outdoor environmentaltemperatures. Deformation of the seal film can result in diminishedretroreflective performance.

The seal film typically has a relatively low glass transitiontemperature for cold temperature flexibility and impact resistance. TheTg of the seal film is preferably less than 25° C., more preferably lessthan 10° C. It is typically preferred that the seal film has a meltindex of less than 25 g/10 min as measured according to ASTM D 1238.Alkylene copolymers with high comonomer contents and melt indices aregenerally more readily melt bonded. However, higher melt indicies canresult in diminished retroreflective performance.

In the case of commercially available copolymers or terpolymers, thesupplier may report the vinyl acetate or other comonomer content.Commercially available films as well as materials suitable for makingfilms can also be analyzed by various known qualitative and quantitativetechniques to determine the alkylene, vinyl acetate, and alkyl(meth)acrylate content such as nuclear magnetic resonance, gaschromatography, mass spectrophotometry, and FT-infrared analysis.

The seal film, cube-corner, or body layer composition may optionallycomprise one or more reactive (e.g. ethylenically unsaturated)ingredients and/or one or more non-reactive ingredients. Variousadditives such as solvent, chain transfer agents, colorants (e.g. dyes),antioxidants, light stabilizers, UV absorbers, processing aids such asantiblocking agents, releasing agents, lubricants, and other additivesmay be added to the body portion or cube-corner elements or seal film asdescribed in U.S. Pat. No. 5,450,235 incorporated herein by reference.

In some embodiments, the seal film further comprises at least onepigment, dye, or combination thereof. It is appreciated that variousopacifying agent can be employed in the seal film to improve thewhiteness of the sheeting. In at least some embodiments, it is preferredto incorporate from about 5 wt-% to about 20 wt-% or 30 wt-% of a (e.g.white) pigment into the seal film. A pigment mixture of 20 wt-% of anEVA resin with 80 wt-% TiO₂ commercially available from PolyOneCorporation, Avon Lake, Ohio under the trade designation “4048 WhiteVAC” is particularly suitable for addition to ethylene vinyl acetatecopolymer based seal films. Since the inclusion of pigment can reduceadhesion, it is also contemplated to employ a multilayered film whereinthe seal film layer contacting the body layer or cube-corner elements islight transmissive and one or more outer layers includes pigment.

Cube-corner retroreflective sheetings of the invention can be made by:(a) forming a plurality of cube-corner elements from a lighttransmissible material; and (b) securing a body layer to the pluralityof cube-corner elements. The sheeting can be made according to a varietyof known (or later discovered) methods for making cube-corner sheeting,see, for example, U.S. Pat. Nos. 3,689,346; 3,811,983; 4,332,847;4,601,861; 5,491,586; 5,642,222 and 5,691,846; incorporated herein byreference.

In one embodiment, the method generally comprises providing a (e.g.heated) electroplated nickel tool having a molding surface with aplurality of cavities suitable for forming desired microstructureelements (e.g., cube corner elements of a retroreflective article) andapplying to the molding surface a flowable (e.g. curable) resincomposition in amount sufficient to at least fill the cavities. The(exposed substantially planar) resin composition surface is thencontacted with a body layer film followed by curing the resin to form acomposite sheeting comprising an array of microstructure elements (e.g.,cube corner elements) bonded to the overlay film. The composite sheetingis removed from the tool followed by applying mechanical stress to thesheeting so as to cause a fractured separation of substantially eachindividual microstructure element from surrounding microstructureelements, if they were connected by a land. Alternatively, the sheetingmay be fractured such that a plurality of cube corner segments areformed, each segment comprising two or more cube corner elements. (Seefor example U.S. Pat. No. 6,318,867.)

The seal film may be bonded in part or solely to the cube-cornerelements. As shown in FIG. 1, as a result of the decoupling of cubecorner elements provided on flexible body layers, the sealing layer canbe adhered, at least in part, directly to the body layer betweenindependent cube corner elements. Illustrative examples of sealingtechniques include radio frequency welding, a conductive heat sealingprocess, ultrasonic welding, and reactive components, e.g., a sealingmaterial that will develop a bond to the overlay film. Selection of asealing approach will depend in large part on the nature of the sealinglayer and body layer.

The seal films described herein, particularly, the monolithic films lendthemselves well to fusing via relatively simple and commonly availablethermal techniques. The general practice followed in the art for sealinga thermoplastic layer to a retroreflective cube corner material is touse thermal embossing techniques which result in a form of “chain link”pattern of sealed zones which create sealed pockets of a plurality ofindividual cube corner elements. Closer inspection of a portion of a legor “link” of a thermally sealed area indicates that for thermoplasticcube corner elements, the thermal fusion process results in significantdistortion of the cube corner elements in fusion zones. This type ofthermal distortion of the sealing legs typically extends well beyond thezone of actual sealing due to conductive effects. If an appreciablenumber of individual cube corner elements in the material are sodistributed, the overall optical properties of the sheeting can decreasesignificantly, e.g., 30 to 40 percent, in comparison to unsealedsheeting.

Radio frequency (“RF”) welding is an alternative to thermal fusion. Whena radio frequency field is applied to a thermoplastic polymer with polargroups, the tendency of the polar groups to switch orientation in phasewith the radio frequency determines the degree to which RF energy isabsorbed and converted to kinetic motion of the polar group. Thiskinetic energy is conducted as heat to the entire polymer molecule; ifenough RF energy is applied, the polymer will heat sufficiently to melt.Further information concerning radio frequency bonding of seal films isdescribed in U.S. Pat. No. 5,691,856.

The interface (16 of FIG. 1) between the body layer and the seal film(e.g. layer) or unstructured surface of the (e.g. cube-corner)microstructure layer typically include an adhesion promoting surfacetreatment. The interface between the body layer and cube-corner may alsoinclude an adhesion promoting agent. Various adhesion promoting surfacetreatments are known and include for example, mechanical roughening,chemical treatment, (air or inert gas such as nitrogen) corona treatment(such as described in US2006/0003178A1, plasma treatment, flametreatment, and actinic radiation. Alternatively or in addition thereto,the adhesion promoting surface treatment may include the application ofa tie layer or primer layer. For example, a polyurethane primer layercan be employed by coating and drying an aliphatic polyester urethanedispersion commercially available from K.J. Quinn & Co., Seabrook, N.H.under the trade designation “QC 4820”. The interfaces may comprise anycombination of adhesion promoting surface treatments.

The cube-corner elements tend to be hard and rigid. The polymericcomposition may be thermoplastic, yet particularly in the case offlexible retroreflective sheeting is preferably a reaction product of apolymerizable (i.e. crosslinkable) resin. The elastic modulus of thecomposition of the cube-corner elements is typically greater than 16×10⁸pascals, preferably greater than 18×10⁸ pascals, and more preferably isgreater than 25×10⁸ pascals. The term “elastic modulus” as used hereinmeans the elastic modulus determined according to ASTM D882-75b usingStatic Weighing Method A with a 12.5 centimeter (5 inch) initial gripseparation, a 2.5 centimeter (1 inch) sample width, and a 2.5centimeter/minute (1 inch/minute) rate of grip separation.

For embodiments wherein the microstructured article is flexible, thebody layer comprises a low elastic modulus polymer for easy bending,curling, flexing, conforming, or stretching. The body layer typicallyhas an elastic modulus less than 13×10⁸ pascals. The elastic modulus maybe less than 7×10⁸ pascals, less than 5×10⁸ pascals or less than 3×10⁸pascals. Generally, the body layer typically has a glass transitiontemperature that is typically less than 25° C. The body layer typicallyhas a Vicat softening temperature that is at least 50° C. Preferredpolymeric materials used in the body layer are resistant to degradationby UV light radiation so that the retroreflective sheeting can be usedfor long-term outdoor applications.

The resin composition (and process conditions) of the cube-cornerelements is preferably chosen such that the resin is capable ofpenetrating the overlay film and then cured in situ or otherwisesolidified, such that after curing an interpenetrating network betweenthe material of the cube corner elements and the material of the overlayfilm is formed as described in U.S. Pat. No. 5,691,856. When theretroreflective sheeting is examined with an electron microscopy, it ispreferred that a blurry boundary rather than a clear interface isobserved between the body layer (e.g. film) and the cube cornerelements.

During curing or solidification of the cube corner composition,depending on the composition of the cube corner material, individualcube corner elements may experience a certain degree of shrinking. Ifthe elastic modulus of the overlay film is too high, torsional stressescan be applied to the cube corner elements if they shrink during curing.If the stresses are sufficiently high, then the cube corner elements canbecome distorted with a resulting degradation in optical performance.When the elastic modulus of the overlay film is sufficiently lower thanthe modulus of the cube corner element material, the overlay film candeform along with the shrinking of cube corner elements without exertingsuch deformational stresses on the cube corner elements that would leadto undesirable degradation of the optical characteristics.

Thermoplastic compositions employed for forming the cube-corner elementstypically have a low linear mold shrinkage, i.e. less than 1 percent. Asdescribed in U.S. Pat. No. 5,691,845, the cube corner polymerizableresin compositions typically shrink upon curing. Preferably the resinwill shrink at least 5 percent by volume when cured, more preferablybetween 5 and 20 percent by volume, when cured. The use of resincompositions that shrink is amenable to obtaining minimal or no landthickness.

In general, the modulus differential between the overlay film and thecube corner elements is typically on the order of 1.0 to 1.5×10⁷ pascalsor more. As the height of the cube corner elements diminishes, it ispossible for this modulus differential to reach the low end of thisrange presumably because the smaller cube corner elements do not undergoas great of shrinkage during curing.

Various polymeric film substrates comprised of various thermosetting orthermoplastic polymers are suitable for use as the body layer. The bodylayer may be a single layer or multi-layer film.

Illustrative examples of polymers that may be employed as the body layerfilm for flexible retroreflective articles include (1) fluorinatedpolymers such as poly(chlorotrifluoroethylene),poly(tetrafluoroethylene-co-hexafluoropropylene),poly(tetrafluoroethylene-co-perfluoro(alkyl)vinylether), poly(vinylidenefluoride-co-hexafluoropropylene); (2) ionomeric ethylene copolymerspoly(ethylene-co-methacrylic acid) with sodium or zinc irons such asSURLYN-8920 Brand and SURLYN-9910 Brand available from E.I. duPontNemours, Wilmington, Del.; (3) low density polyethylenes such as lowdensity polyethylene; linear low density polyethylene; and very lowdensity polyethylene; plasticized vinyl halide polymers such asplasticized poly(vinychloride); (4) polyethylene copolymers includingacid functional polymers such as poly(ethylene-co-acrylic acid) “EAA”,poly(ethylene-co-methacrylic acid) “EMA”, poly(ethylene-co-maleic acid),and poly(ethylene-co-fumaric acid); acrylic functional polymers such aspoly(ethylene-co-alkylacrylates) where the alkyl group is methyl, ethyl,propyl, butyl, et cetera, or CH₃(CH₂)_(n)— where n is 0 to 12, andpoly(ethylene-co-vinylacetate) “EVA”; and (5) (e.g.) aliphaticpolyurethanes.

The body layer is preferably an olefinic polymeric material, typicallycomprising at least 50 wt-% of an alkylene having 2 to 8 carbon atomswith ethylene and propylene being most commonly employed.

Other body layers include for example poly(ethylene naphthalate),polycarbonate, poly(meth)acrylate (e.g., polymethyl methacrylate or“PMMA”), polyolefins (e.g., polypropylene or “PP”), polyesters (e.g.,polyethylene terephthalate or “PET”), polyamides, polyimides, phenolicresins, cellulose diacetate, cellulose triacetate, polystyrene,styrene-acrylonitrile copolymers, cyclic olefin copolymers, epoxies, andthe like.

Polymerizable resins suitable for forming the array of cube cornerelements may be blends of photoinitiator and at least one compoundbearing an acrylate group. Preferably the resin blend contains amonofunctional, a difunctional, or a polyfunctional compound to ensureformation of a cross-linked polymeric network upon irradiation.

Illustrative examples of resins that are capable of being polymerized bya free radical mechanism that can be used herein include acrylic-basedresins derived from epoxies, polyesters, polyethers, and urethanes,ethylenically unsaturated compounds, isocyanate derivatives having atleast one pendant acrylate group, epoxy resins other than acrylatedepoxies, and mixtures and combinations thereof. The term acrylate isused here to encompass both acrylates and methacrylates. U.S. Pat. No.4,576,850 (Martens) discloses examples of crosslinked resins that may beused in cube corner element arrays of the present invention.

Ethylenically unsaturated resins include both monomeric and polymericcompounds that contain atoms of carbon, hydrogen and oxygen, andoptionally nitrogen, sulfur, and the halogens may be used herein. Oxygenor nitrogen atoms, or both, are generally present in ether, ester,urethane, amide, and urea groups. Ethylenically unsaturated compoundspreferably have a molecular weight of less than about 4,000 andpreferably are esters made from the reaction of compounds containingaliphatic monohydroxy groups, aliphatic polyhydroxy groups, andunsaturated carboxylic acids, such as acrylic acid, methacrylic acid,itaconic acid, crotonic acid, iso-crotonic acid, maleic acid, and thelike. Such materials are typically readily available commercially andcan be readily cross linked. Some illustrative examples of compoundshaving an acrylic or methacrylic group that are suitable for use arelisted below:

(1) Monofunctional Compounds:

-   ethylacrylate, n-butylacrylate, isobutylacrylate,    2-ethylhexylacrylate, n-hexylacrylate, n-octylacrylate, isooctyl    acrylate, bornyl acrylate, tetrahydrofurfuryl acrylate,    2-phenoxyethyl acrylate, and N,N-dimethylacrylamide;

(2) Difunctional Compounds:

-   1,4-butanediol diacrylate, 1,6-hexanediol diacrylate,    neopentylglycol diacrylate, ethylene glycol diacrylate,    triethyleneglycol diacrylate, tetraethylene glycol diacrylate, and    diethylene glycol diacrylate; and

(3) Polyfunctional Compounds:

-   trimethylolpropane triacrylate, glyceroltriacrylate, pentaerythritol    triacrylate, pentaerythritol tetraacrylate, and    tris(2-acryloyloxyethyl)isocyanurate.

Monofunctional compounds typically tend to provide faster penetration ofthe material of the overlay film and difunctional and polyfunctionalcompounds typically tend to provide more crosslinked, stronger bonds atthe interface between the cube corner elements and overlay film.

Some representative examples of other ethylenically unsaturatedcompounds and resins include styrene, divinylbenzene, vinyl toluene,N-vinyl formamide, N-vinyl pyrrolidone, N-vinyl caprolactam, monoallyl,polyallyl, and polymethallyl esters such as diallyl phthalate anddiallyl adipate, and amides of carboxylic acids such asN,N-diallyladipamide.

Cationically polymerizable materials including but are not limited tomaterials containing epoxy and vinyl ether functional groups may be usedherein. These systems are photoinitiated by onium salt initiators, suchas triarylsulfonium, and diaryliodonium salts.

The polymerizable resin may comprise a combination of at least onedifunctional epoxy (meth)acrylate, at least one difunctional(meth)acrylate monomer, at least one polyfunctional compound having atleast three (meth)acrylate groups, and optionally a nitrogen-containingingredient.

The difunctional epoxy (meth)acrylate, as well as the difunctional(meth)acrylate monomer may be present in the polymerizable compositionin an amount of at least about 5 wt-%, 10 wt-%, and any amount therebetween. Typically, the amount of such difunctional (meth)acrylatemonomer does not exceed about 40 wt-%. One exemplary epoxy diacrylate iscommercially available from Cytek under the trade designation “Ebecryl3720”.

The polyfunctional compound is typically present in the polymerizablecomposition in an amount of at least about 10 wt-% (e.g. 15 wt-%, 20wt-%, 25 wt-%, 30 wt-%, 35 wt-%, 40 wt-% and any amount there between).Typically, the amount of polyfunctional compound is not greater thanabout 70 wt-%.

Since methacrylate groups tend to be less reactive than acrylate groups,acrylate functionality is preferred.

Radiation (e.g. UV) curable compositions generally include at least onephotoinitiator. The photoinitiator or combination of photoiniators canbe used at a concentration of about 0.1 to about 10 weight percent. Morepreferably, the photoinitiator or combination thereof is used at aconcentration of about 0.2 to about 3 wt-%.

In general the photoinitiator(s) are at least partially soluble (e.g. atthe processing temperature of the resin) and substantially colorlessafter being polymerized. The photoinitiator may be (e.g. yellow)colored, provided that the photoinitiator is rendered substantiallycolorless after exposure to the UV light source.

Suitable photoinitiators include monoacylphosphine oxide andbisacylphosphine oxide. Commercially available mono or bisacylphosphineoxide photoinitiators include 2,4,6-trimethylbenzoydiphenylphosphineoxide, commercially available from BASF (Charlotte, N.C.) under thetrade designation “Lucirin TPO”; ethyl-2,4,6-trimethylbenzoylphenylphosphinate, also commercially available from BASF under the tradedesignation “Lucirin TPO-L”; andbis(2,4,6-trimethylbenzoyl)-phenylphosphine oxide commercially availablefrom Ciba Specialty Chemicals under the trade designation “Irgacure819”. Other suitable photoinitiators include2-hydroxy-2-methyl-1-phenyl-propan-1-one, commercially available fromCiba Specialty Chemicals under the trade designation “Darocur 1173” aswell as other photoinitiators commercially available from Ciba SpecialtyChemicals under the trade designations “Darocur 4265”, “Irgacure 651”,“Irgacure 1800”, “Irgacure 369”, “Irgacure 1700”, and “Irgacure 907”.

Free radical scavengers or antioxidants may be used, typically, at about0.01 to 0.5 weight percent. Illustrative examples of suitableantioxidants include hindered phenolic resins such as those availableunder the trade designations “Irganox 1010”, “Irganox 1076”, “Irganox1035”, and “Irgafos 168” from Ciba-Geigy Corp.

When thermoplastic polymers are used in the (e.g. cube) microstructures,the glass transition temperature generally is greater than 80° C., andthe softening temperature is typically greater than 150° C. Generally,the thermoplastic polymers used in the cube-corner layer are amorphousor semi-crystalline.

Examples of thermoplastic polymers that may be used in the cube-cornerelements include acrylic polymers such as poly(methyl methacrylate);polycarbonates; cellulosics such as cellulose acetate,cellulose(acetate-co-butyrate), cellulose nitrate; epoxies; polyesterssuch as poly(butylene terephthalate), poly(ethylene terephthalate);fluoropolymers such as poly(chlorofluoroethylene), poly(vinylidenefluororide); polyamides such as poly(caprolactam), poly(amino caproicacid), poly(hexamethylene diamine-co-adipic acid), poly(amide-co-imide),and poly(ester-co-imide); polyetherketones; poly(etherimide);polyolefins such as poly(methylpentene); poly(phenylene ether);poly(phenylene sulfide); poly(styrene) and poly(styrene) copolymers suchas poly(styrene-co-acrylonitrile),poly(styrene-co-acrylonitrile-co-butadiene); polysulfone; siliconemodified polymers (i.e., polymers that contain a small weight percent(less than 10 weight percent) of silicone) such as silicone polyamideand silicone polycarbonate; fluorine modified polymers such asperfluoropoly(ethyleneterephthalate); and mixtures of the above polymerssuch as a poly(ester) and poly(carbonate) blend, and a fluoropolymer andacrylic polymer blend.

The (e.g. polymerizable or thermoplastic) resin of the cube-cornerelements may comprise a nitrogen-containing ingredient, as described inU.S. Ser. No. 60/745033, filed Apr. 18, 2006; incorporated herein byreference. Preferred nitrogen-containing ingredients include for examplepolymerizable amine-containing ingredients, (meth)acrylate functionalnitrogen-containing ingredients, and nitrogen-containing polymers.

A common method for improving the uniformity of total light return (TLR)with respect to orientation is tiling, i.e. placing a multiplicity ofsmall tooling sections in more than one orientation in the finalproduction, as described for example in U.S. Pat. No. 4,243,618 (VanArnam), U.S. Pat. No. 4,202,600; and U.S. Pat. No. 5,936,770 (Nestegardet al.). The resulting sheeting has a first array of cube-cornerelements having a different orientation than an adjacent array ofcube-corner elements.

The roll of retroreflective sheeting formed has a width bound bylongitudinal edges of the roll and a microstructured surface having anarray of cube-corner elements, e.g. defined by three mutuallyintersecting grooves. Depending on the orientation of the tool one ofthe grooves may be substantially perpendicular, parallel, or at an anglebetween 0° and 90° to the longitudinal edge of the roll of sheeting.

The retroreflective sheeting is useful for a variety of uses such astraffic signs, pavement markings, vehicle markings and personal safetyarticles, in view of its flexibility is combination with retroreflectedbrightness. The coefficient of retroreflection, R_(A), may be measuredaccording to US Federal Test Method Standard 370 at −4° entrance, 0°orientation, at various observation angles. Retroreflective sheetingtypically has a coefficient of retroreflection, R_(A), at −4° entrance,0° orientation, and an observation angle of 0.2° of at least 50, 100,150, 200, or 250 candelas/lux/m².

Due to the flexibility of the retroreflective sheeting, the sheeting isamendable for application to flexible substrates such as canvas andother fabrics, corrugated and riveted surfaces, as well as curvedsurfaces having a simple or compound curve. The flexible retroreflectivesheeting is also amenable for application to devices subject to thermalexpansion and contraction (e.g. traffic devices such as barrels, cones).

Features and advantages of this invention are further illustrated in thefollowing examples. It is to be expressly understood, however, thatwhile the examples serve this purpose, the particular ingredients andamounts used as well as other conditions and details are not to beconstrued in a manner that would unduly limit the scope of thisinvention.

EXAMPLES 1-5

Articles comprising the seal films of Examples 1-5 in Table 1 wereprepared by combining two constructions. The First Construction was theseal film on a polyethylene terephthalate (PET) carrier; the SecondConstruction was cube corner microstructures laminated to the primer ofan EAA film with the primer on one side and a PET carrier on the otherside.

The First Construction of Examples 1-5 was prepared by extruding eachresin (available from E. I. DuPont de Nemours and Company (“DuPont”;Wilmington, Del.)) in Table 1 onto a PET carrier film approximately 15cm (6 in) wide and 0.05 mm (0.002 in) thick. The melt index, melt pointand % vinyl acetate content of each resin in Table 1 was obtained fromproduct data sheets provided on the dupont.com website.

Each resin in Table 1 was fed as pellets into a 1.9 cm (3/4 in) singlescrew extruder available from C.W. Brabender Instruments Inc., SouthHackensack, N.J. The extruder temperature profile was from 140° C. (284°F.) to 175° C. (347° F.) resulting in a melt temperature of about 175°C. (347° F.). As the molten resin exited the extruder, it passed througha horizontal die (Ultraflex—40; available from Extrusion Dies IndustriesLLC, Chippewa Falls, Wis.) and was cast onto the PET carrier describedabove. The PET carrier was traveling at approximately 3 meters/min (10ft/min.). The resulting molten seal film on the PET carrier was runbetween a rubber roll and a chilled steel backup roll to solidify themolten resin into a layer having a thickness of approximately 0.075 mm(0.003 in). Each resultant First Construction was wound to form a roll.

The Second Construction was prepared by casting Primacor 3440 (EAA;available from Dow Chemical Company, Midland, Mich.) as a film at athickness of 4 mils onto a PET carrier prepared using the extrusionprocess described above for the First Construction. The EAA surface wascoated with QC 4820 primer (an aliphatic polyester urethane availablefrom K.J. Quinn & Co, Seabrook, N.H.) such that it had a final driedthickness of approximately 2.5 microns (0.0001 inch).

Cube corner microstructures were provided on a body layer as describedand illustrated in FIG. 5 of U.S. Pat. No. 5,691,846. The cube cornermicrostructures (prior to separating the structure into individualcubes) had 3 sets of intersecting grooves as shown in FIG. 2 having apitch (i.e. primary groove spacing) of 0.007″ with base triangleapertures of 55.5/55.5/69 degrees resulting in the height of the cubecorner elements being 76.2 microns (3.5 mil).

The cube corner microstructures were prepared using a resin compositionformed by combining 25 wt-% bisphenol A epoxy diacrylate, commerciallyavailable from Cytek under the trade designation “Ebecryl 3720”, 12 wt-%dimethylaminoethyl acrylate (“DMAEA”), 38 wt-% TMPTA (trimethylolpropane triacrylate) and 25 wt-% 1,6 HDDA (hexanediol diacrylate). Theformulation had 0.5 pph of TPO (2,4,6-trimethylbenzoyl diphenylphosphineoxide) photoinitiator.

The resin composition was cast at room temperature at 15 fpm onto ametal tool heated to 140° F. The resin composition filled the cavitiesof the cube corner microstructures in the tool via a rubber nip rollerhaving a gap set to fill the cavities of the embossed pattern on thetool and minimize the amount of resin on the land area of the tool. Theprimer layer of the primer/EAA film/PET carrier was brought in contactwith the cube corner microstructures of the resin. The cube cornermicrostructure resin was cured through the PET carrier/EAA film/primeron the tool with one Fusion D UV lamp (available from Fusion Systems,Rockville, Md.) set at 360 W/in. Dichroic filters were used in front ofthe UV lamps to minimize IR heating of the construction. After curing ofthe cube corner microstructures on the tool, the composite was removedfrom the tool and the polymerizable resin side of the composite with thecube corner elements was irradiated by a Fusion D UV lamp operating at600 W/in to provide a post-UV irradiation cure. The composite was passedthrough an oven set at 150° F. to relax the stresses in the film.

Each of the First Constructions (seal film/PET carrier) described abovewas corona treated at an energy of about 2 J/cm² (0.25 kW at 10 fpm). A2 inch wide strip of 3M™ Polyester Tape 8403 (available from 3MCompany), applied across the width of the construction and flush withthe edge of the sample, was placed on both the seal film of the FirstConstruction and the cube corner microstructures of the SecondConstruction to form tape tabs. The tape tabs would to be used later toinitiate the peeling process for the 90 degree peel adhesion test.

The First Construction and the Second Construction were laminated usinga 12 inch wide laminator composed of a rubber roll and a heated metalemboss roll. The emboss roll had a hexagonal seal pattern thereon. Thelamination pressure was 25 psi and line speed was 15 fpm. The FirstConstruction and the Second Construction were fed through the nip of therolls such that the tape tab on the seal film of the First Constructionand the tape tab on the cube corner microstructures of the SecondConstruction were aligned and face to face to eliminate sealing in thetape tab areas and allow peel initiation for later testing. The PETcarrier side of the First Construction was placed independently againstthe heated emboss roll at temperatures of 300° F. and 375° F. The PETcarrier side of the Second Construction was against a rubber roll whichhad a temperature of about 115° F. due to contact against the heatedemboss roll. The article exiting the laminator had the seal film bondedto the cube corner microstructures and 2 tape tabs present to allow peeladhesion initiation.

After the article was allowed to cool to room temperature, the PETcarrier was removed from the seal film and the seal film was coronatreated at an energy of about 2 J/cm² (0.25 kW at 10 fpm). A 3 mil thickacrylic transfer pressure sensitive adhesive similar to that describedin U.S. Pat. No. 6,677,030 on a release liner was laminated to the sealfilm using a non-heated laminator.

For each Example in Table 1, two test samples, each about 1 inch wideand 8 inches long, were cut from each article, leaving the tape tabsexposed at one end of each test sample. The release liner on thetransfer adhesive was removed and the exposed adhesive on the seal filmwas placed on an untreated 2.75 inch×11 inch aluminum panel (Q Panel LabProducts, Cleveland, Ohio) and rolled back and forth twice with a 2 lb.rubber roller at about 100 inches per minute. The article on thealuminum panel was conditioned at room temperature for 24 hours prior toadhesion testing.

The PET carrier on the EAA film of the article applied to the aluminumpanel was removed and a 1 inch wide strip of Scotch® Filament Tape 898(available from 3M Company) was applied over the tape tab and exposedEAA film of the entire article to prevent stretching of the extensiblelayers in the article. The aluminum panel was mounted on the slidingtable of an Instron tensile tester, ensuring maintenance of a 90 degreepeel angle during adhesion testing. The tape tab with the filament tapewas placed in the upper jaw of the tensile tester. Peel adhesion testingwas performed according to ASTM D3330 at a crosshead speed of 12inches/min. The peel adhesion values provided in Table 1 are the averageof two samples independently made at emboss roll temperatures of 300° F.and 375° F.

TABLE 1 Melt Index at Melt Peel Adhesion - Peel Adhesion - 190° C./2.16kg Point % Vinyl 300° F. Emboss 375° F. Emboss Ex. Resin (g/10 min) (°C.) Acetate Roll (lb/in) Roll (lb/in) 1 ELVAX 3124 7 98 9 1.37 2.75 2ELVAX 3134Q 8 95 12 2.59 4.53 3 ELVAX 3174 8 86 18 4.43 6.92 4 ELVAX3170 2.5 87 18 2.50 3.43 5 ELVAX 3190 2 77 25 2.84 3.95

The data in Table 1 show that at comparable melt index values the peeladhesion increased as the vinyl acetate content increased (exhibited byExamples 2 and 3). The data also show that at comparable vinyl acetatevalues the peel adhesion decreased as the melt index decreased(exhibited by Examples 3 and 4).

EXAMPLES 6-10 AND COMPARATIVE EXAMPLE C1

Examples 6-10 and Comparative Example C1 were prepared as described forExamples 1-5, except that the emboss roll temperature was 315° F. andthe resins in Table 2 were used to prepare the seal film for eachexample.

Comparative Example C1 was prepared as described for Examples 6-10,except that Primacor 3440 was used as the seal film resin. The Primacor3440 seal film did not adhere to the cube corner microstructures whenthe First construction and the Second Construction were laminated toform an article.

Samples were prepared and 90 degree peel adhesion measured as describedin Examples 1-5. The peel adhesion values are provided in Table 2. Thedescription of the resin, melt index, melt point and Vicat softeningpoint information of Examples 6-10 in Table 2 were obtained from productdata sheets provided on the dupont.com website.

TABLE 2 Melt Index at Melt Vicat Peel Adhesion - Description of the 190°C./2.16 kg Point Softening 315° F. Emboss Ex. Resin Resin (g/10 min) (°C.) Point (° C.) Roll (lb/in) 6 BYNEL 3126 Acid/acrylate- 8.1 87 60 4.87modified EVA 7 BYNEL 2014 Acid-modified 7.9 86 57 4.37 ethylene acrylate8 BYNEL 21E533 Anhydride- 7.7 83 50 8.72 modified ethylene acrylate 9BYNEL 22E757 Modified acrylate 8 92 54 8.34 copolymer 10 BYNEL 3101Acid/acrylate- 3.2 87 65 4.15 modified EVA C1 PRIMACOR 3440 EAA 0

The data in Table 2 show that the seal films of Examples 6-10 adheredwell to the cube corner microstructures with Examples 8 and 9 having thebest adhesion. The seal film of Comparative Example C1 did not adhere tothe cube corner microstructures.

EXAMPLES 11-15 AND COMPARATIVE EXAMPLE C2

Examples 11-15 and Comparative Example C2 were prepared as described forExamples 1-5, except that the emboss roll temperature was 300° F. andthe seal films were prepared using 80 wt-% of the resin in Table 3 and20 wt-% 4048 White VAC (a mixture of 20 wt-% of an EVA resin with 80wt-% TiO2; available from PolyOne Corporation, Avon Lake, Ohio).

Comparative Example C2 was prepared as described for Examples 11-15,except that Krystalgran PNO3 (a polyurethane available form HuntsmanPolyurethanes, Houston, Tex.) was used as the seal film resin. Sampleswere prepared and 90 degree peel adhesion measured as described inExamples 1-5. The peel adhesion values are provided in Table 3.

TABLE 3 Peel Adhesion - Resin with 20% 300° F. Emboss Roll Ex. TiO2/EVA(lb/in) 11 BYNEL 3126 2.31 12 BYNEL 2014 1.97 13 BYNEL 21E533 5.48 14BYNEL 22E757 5.71 15 BYNEL 3101 1.86 C2 KRYSTALGRAN PNO3 0.32

The data in Table 3 show that the seal films of Examples 11-15 adheredwell to the cube corner microstructures with Examples 13 and 14 havingthe best adhesion. The seal film of Comparative Example C2 (apolyurethane) had very low adhesion to the cube corner microstructures.

EXAMPLE 16

Example 16 was prepared as described for Examples 1-5, except that theemboss roll temperature was 300° F. Samples were prepared and 90 degreepeel adhesion measured as described in Examples 1-5. The peel adhesionvalue is provided in Table 4. The description of the resin, melt indexand melt point information of Example 16 in Table 4 were obtained fromproduct data sheets provided on the dupont.com website.

TABLE 4 Melt Index at Melt Peel Adhesion - 190° C./2.16 kg Point 300° F.Emboss Ex. Resin Description of the Resin (g/10 min) (° C.) Roll (lb/in)16 ELVALOY Ethylene/vinyl acetate/carbon 15 70 5.47 4924 monoxidecopolymer

The peel adhesion value in Table 4 shows that an ethylene/vinylacetate/carbon monoxide terpolymer adhered well to the cube cornermicrostructures when used as a seal film.

EXAMPLE 17 AND COMPARATIVE EXAMPLE C3

Example 17 and Comparative Example C3 were prepared as described forExamples 1-5, except that the emboss roll temperature was 300° F.Example 17 was prepared using 10 wt-% SURLYN 1705-1 (available fromDuPont) and 90 wt-% BYNEL 3126. Samples were prepared and 90 degree peeladhesion measured as described in Examples 1-5. The peel adhesion valuesare provided in Table 5. The description of the resin, melt index, meltpoint and Vicat softening point information of Example C3 in Table 5were obtained from product data sheets provided on the dupont.comwebsite.

TABLE 5 Melt Index at Melt Vicat Peel Adhesion - Description of the 190°C./2.16 kg Point Softening 315° F. Emboss Ex. Resin Resin (g/10 min) (°C.) Point (° C.) Roll (lb/in) 17 10% SURLYN 3.67 1705-1/90% BYNEL 3126C3 SURLYN 1705-1 Zinc ionomer of 5-5 95 65 0.26 ethylene methacrylicacid

The data in Table 5 show that a seal film can be produced by blendingmaterials having different cube corner adhesion properties. In Table 5SURLYN 1705-1 of Comparative Example C3 was a poor seal film material,but when blended with 90 wt-% BYNEL 3126, the blended compositionadhered well to the cube corner microstructures.

The coefficient of retroreflection, R_(A), of the resulting cube-cornersheeting of Example 10 was evaluated according to US Federal Test MethodStandard 370 using an observation angle of 0.2°, an orientation of 0°and an entrance angle of −4°. The average R_(A) of four measurements was639 candelas/lux/m².

1. A flexible retroreflective article comprising a polymeric lighttransmissive body layer having an elastic modulus of less than 7×10⁸pascals; a plurality of cube-corner elements projecting from a majorsurface of the body layer; and a multilayered seal film having a firstfilm layer and a second film layer, the second film layer adhered to atleast portions of the body layer such that the seal film maintains anair interface with the cube-corner elements; the second film layercomprising a thermoplastic polymeric material comprising reactionproducts of alkylene in an amount of at least about 50% by weight andreaction products of at least one non-acidic polar monomer wherein thethermoplastic material has a different melt flow index than the sealfilm layer in contact with the body layer; wherein the seal film layerin contact with the body layer is a thermoplastic polymeric materialcomprising reaction products of alkylene in an amount of at least about50% by weight and reaction products of at least one non-acidic polarmonomer and the thermoplastic polymeric material comprises acidmodification, anhydride modification, carbon monoxide modification, or acombination thereof.
 2. The flexible retroreflective article of claim 1wherein the alkylene has 2 to 8 carbon atoms.
 3. The flexibleretroreflective article of claim 2 wherein the alkylene is ethylene. 4.The flexible retroreflective article of claim 1 wherein the non-acidicmonomer is selected from vinyl acetate, alkyl(meth)acrylate monomers,and mixtures thereof.
 5. The flexible retroreflective article of claim 4wherein the alkyl(meth)acrylate has an alkyl group having 1 to 8 carbonatoms.
 6. The flexible retroreflective article of claim 5 wherein thealkyl (meth)acrylate is selected from the group consisting of methylacrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butylacrylate, butyl methacrylate and mixtures thereof.
 7. The flexibleretroreflective article of claim 1 wherein the seal film comprises acopolymer or terpolymer of alkylene and at least one non-acid polarcomonomer selected from vinyl acetate; alkyl(meth)acrylate monomers, andmixtures thereof.
 8. The flexible retroreflective article of claim 7wherein the copolymer or terpolymer comprises about 10 wt-% to about 40wt-% of vinyl acetate, alkyl(meth)acrylate monomers, and mixturesthereof.
 9. The flexible retroreflective article of claim 1 wherein theseal film is selected from acid- or anhydride-modified EVA, acid oranhydride-/acrylate-modified EVA, acid- or anhydride-modified ethyleneacrylate polymers, and EVA carbon monoxide terpolymers.
 10. The flexibleretroreflective article of claim 1 wherein the seal film comprises ablend of at least two thermoplastic polymers and the blend comprisesreaction products of alkylene in an amount of at least about 50% byweight and reaction products of vinyl acetate, alkyl(meth)acrylatemonomers, and mixtures thereof.
 11. The flexible retroreflective articleof claim 10 wherein the blend comprises a thermoplastic polymer selectedfrom ionomeric ethylene copolymers, low density polyethylene, EAA, EMA,and polyurethanes.
 12. The flexible retroreflective article of claim 1wherein the seal film has a melt index of less than 25 g/10 min asmeasured according to ASTM D
 1238. 13. The flexible retroreflectivearticle of claim 1 wherein the seal film further comprises at least onepigment, dye, or combination thereof.
 14. The flexible retroreflectivearticle of claim 1 wherein the seal film is monolithic.
 15. The flexibleretroreflective article of claim 1 wherein the second film layercomprises the same thermoplastic polymeric material as claim 1 andfurther comprises 5 wt-% to 30 wt-% of pigment.
 16. The flexibleretroreflective article of claim 1 wherein the seal film contacts thebody layer or cube film at an interface and the interface furthercomprises an adhesion promoting surface treatment.
 17. The flexibleretroreflective article of claim 16 wherein the adhesion promotingsurface treatment comprises a prime layer, corona treatment, or acombination thereof.
 18. The flexible retroreflective article of claim 1wherein the body layer comprises a polymeric material selected fromionomeric ethylene copolymers, low density polyethylenes, polyethylenecopolymers, plasticized poly(vinylchloride), polyurethane, and mixturesthereof.
 19. The flexible retroreflective article of claim 1 wherein thebody layer is olefinic.
 20. A retroreflective article that comprises: aplurality of cube-corner elements; and a multilayered seal film layerhaving a first film layer and a second film layer, the second film layeradhered to portions of the cube-corner elements such that the seal filmmaintains an air interface with the cube-corner elements, the secondfilm layer comprising a thermoplastic polymeric material comprisingreaction products of alkylene in an amount of at least about 50% byweight and reaction products of at least one non-acidic polar monomerwherein the thermoplastic material has a different melt flow index thanthe seal film layer in contact with the body layer; wherein the sealfilm layer in contact with the cube-corner elements is a thermoplasticpolymeric material comprising reaction products of alkylene in an amountof at least about 50% by weight and reaction products of at least onenon-acidic polar monomer and the thermoplastic polymeric materialcomprises acid modification, anhydride modification, carbon monoxidemodification, or a combination thereof.
 21. The retroreflective articleof claim 20 wherein the cube-corner elements project from an integralbody layer.
 22. The retroreflective article of claim 20 wherein thecube-corner elements compose a thermoplastic polymeric material.
 23. Theflexible retroreflective article of claim 20 wherein the cube-cornerelements comprise the reaction product of a polymerizable resincomposition.
 24. The flexible retroreflective article of claim 20wherein the cube-corner elements comprise at least onenitrogen-containing ingredient.
 25. A method of making a retroreflectivearticle comprising: providing a light transmissive polymeric body layercomprising a plurality of cube-corner elements projecting from a majorsurface of the body layer; and thermally bonding a multilayered sealfilm, having a first film layer and a second film layer, to portions ofthe body layer or to the cube-corner elements such that the seal filmmaintains an air interface with the cube-corner elements, the secondfilm layer comprising a thermoplastic polymeric material comprisingreaction products of alkylene in an amount of at least about 50% byweight and reaction products of at least one non-acidic polar monomerwherein the thermoplastic material has a different melt flow index thanthe seal film layer in contact with the body layer; wherein the sealfilm layer in contact with the body layer or cube-corner elements is athermoplastic polymeric material comprising reaction products ofalkylene in an amount of at least about 50% by weight and reactionproducts of at least one non-acidic polar monomer and the thermoplasticpolymeric material comprises acid modification, anhydride modification,carbon monoxide modification, or a combination thereof.
 26. Amicrostructured article that comprises a plurality of polymericmicrostructured elements; and a multilayered seal film having a firstfilm layer and a second film layer, the second film layer adhered toportions of the microstructured elements such that the seal filmmaintains an air interface with the microstructured elements, the secondfilm layer comprising a thermoplastic polymeric material comprisingreaction products of alkylene in an amount of at least about 50% byweight and reaction products of at least one non-acidic polar monomerwherein the thermoplastic material has a different melt flow index thanthe seal film layer in contact with the body layer; wherein the sealfilm layer in contact with the microstructured elements is athermoplastic polymeric material comprising reaction products ofalkylene in an amount of at least about 50% by weight and reactionproducts of at least one non-acidic polar monomer and the thermoplasticpolymeric material comprises acid modification, anhydride modification,carbon monoxide modification, or a combination thereof.
 27. Themicrostructured article of claim 1 wherein the seal film is bonded inpart to the cube-corner elements.
 28. The flexible retroreflectivearticle of claim 1 wherein the second film layer comprises a differentthermoplastic polymeric material than the seal film layer in contactwith the body layer.
 29. The flexible retroreflective article of claim28 further comprising a tie layer between the seal film layer and thesecond film layer.